2.85 mm PVOH Mowiflex 3D 1000 water soluble support filament


Mowiflex™ is a water soluble thermoplastic material based on polyvinyl alcohol that enables printing of complex structures even those containing moving parts in one. The support structures are easily dissolved in cold water.

Buy - Prices VAT included
Sample (2 meters) €2,50 €1,25
5 meters €5,50 €2,75


PVOH based filament in natural color.


  • Soluble in cold water, dissolves better than PVA
  • No organic solvents needed
  • Low moisture absorption

  • More filament stiffness 
then PVA
  • High melt flow
  • Adhesion to PLA, PVB, PA, TPU, PETG
  • Ultimaker compatible
  • Biodegradable, TUV certificated

Tech specifications

Nominal diameter 2.85 mm
Warp n.a.
Flexibility n.a.
Break resistance low
Printing temperature ~ 190-210 °C
Glass Transition Temperature 60-65 °C


Mowiflex™ should be printed between 190-210 °C, do not exceed a nozzle temperature of 220 °C and reduce nozzle temperature to <170 °C when temporarily idle. Don’t let the filament in the extruder when idle. Set the heated bed at about 25-70 °C.
Suggested printing speed: 20-50 mm/s.
Keep away from moisture and store in a sealed aluminum bag. Damp material can be dried at 60-80 °C for 6-8 hours in a circulating air dryer.

Melt temperature during extrusion should not exceed 220°C because at higher temperatures the material suffers thermal damage, recognizable by yellow discoloration.
After printing, it is highly recommended to completely purge out Mowiflex™ from the extruder.

Mowiflex™ can be dissolved in pure tap water. Use slightly elevated temperatures (about 30-40 °C) and agitation to accelerate dissolution. Aqueous Mowiflex™ solutions can be disposed to normal waste water treatment plants.


Due to all the different types of hot-end it's extremely difficult to give a temperature advice. Please consider our tips as a starting point to find the temperatures that work well in your setup. You may have to adjust the temperature settings slightly based on your type of printer.